ADVANTAGES
• Fast cure and rapid development of hardness
• High strength and modulus
• Excellent cure at low temperatures
• Reduced tendency to form carbamates with carbon dioxide in the atmosphere during cure
• Very good chemical resistance to distilled water, inorganic acids and alkalies; good against organic acids and alkalies and many organic solvents
APPLICATIONS
• Concrete repair mortars
• Solvent-free and high-solids coatings
• Adhesives
• Tank linings and chemically resistant coatings
• Accelerator for other curing agents
SHELF LIFE
At least 12 months from the date of manufacture in the original sealed container at ambient temperature. Store away from excessive heat and humidity in tightly closed containers.
STORAGE AND HANDLING
Refer to the Material Safety Data Sheet for Ancamine 2636 curing agent.
TYPICAL CURE SCHEDULE
2–7 days at ambient temperature.
| TYPICAL PROPERTIES | |
| Appearance | Yellow Liquid |
| Color (Gardner) | 5 |
| Viscosity at 25°C (mPas) | 300 |
| Amine Value (mg KOH/g) | 360 |
| Specific Gravity @ 25°C [g/ml] | 1.104 |
| Flash Point (Cleveland open cup) (°C) | 138 |
| Hydrogen Equivalent Weight | 78 |
| TYPICAL HANDLING PROPERTIES* | |
| Use Level (phr) | 40 |
| Mixed Viscosity @ 25°C [mPa.s] | 2,040 |
| Gel Time (150g mix @ 25°C) (min) | 11 |
| Thin Film Set Time @ 25°C (hr) | 3 |
| Thin Film Set Time @ 5°C (hr) | 11 |
| TYPICAL HANDLING PROPERTIES*(7 day cure @ 25°C) | |
| Compressive Strength (MPa) | 110 |
| Compressive Modulus (MPa) | 2,600 |
| Flexural Strength (MPa) | 112 |
| Flexural Modulus (MPa) | 3,750 |
| Tensile Strength (MPa) | 70 |
| Tensile Modulus (MPa) | 1,520 |
| Elongation (%) | 4.5 |
| Shore D Hardness | 82 |
* Ancamine 2636 curing agent formulated withstandard Bisphenol-A based (DGEBA, EEW=190) epoxy resin.